250+ TOP MCQs on Phase Transformations in Iron-Carbon Systems and Answers

Materials Science online quiz on “Phase Transformations in Iron-Carbon Systems”.

1. What is the Peritectic reaction at 1495°C?
a) L (0.53% C) + δ(0.09% C) → γ(0.17% C)
b) L (4.3% C) → γ(2.1 % C) + Fe3C (6.67% C)
c) γ (0.8 % C) → α (0.025% C) + Fe3C (6.67% C)
d) L (0.53% C) + δ(0.09% C) → γ (0.8 % C)
Answer: a
Clarification: Peritectic reaction at 1495°C is
L (0.53% C) + δ(0.09% C) → γ(0.17% C).

2. What is the Eutectic reaction at 1146°C?
a) L (0.53% C) + δ(0.09% C) → γ(0.17% C)
b) L (4.3% C) → γ(2.1 % C) + Fe3C (6.67% C)
c) γ (0.8 % C) → α (0.025% C) + Fe3C (6.67% C)
d) L (0.53% C) + δ(0.09% C) → γ (0.8 % C)
Answer: b
Clarification: Eutectic reaction at 1146°C is
L (4.3% C) → γ(2.1 % C) + Fe3C (6.67% C).

3. What is Eutectoid reaction at 727°C?
a) L (0.53% C) + δ(0.09% C) → γ(0.17% C)
b) L (4.3% C) → γ(2.1 % C) + Fe3C (6.67% C)
c) γ (0.8 % C) → α (0.025% C) + Fe3C (6.67% C)
d) L (0.53% C) + δ(0.09% C) → γ (0.8 % C)
Answer: c
Clarification: Eutectoid reaction at 727°C is
γ (0.8 % C) → α (0.025% C) + Fe3C (6.67% C).

4. The eutectic mixture of austenite (γ) and cementite (Fe3C) is called __________
a) Ledeburite
b) Pearlite
c) Hyper and hypo eutectoid steel
d) Cast iron
Answer: a
Clarification: Eutectic reaction at 1146°C is
L (4.3% C) → γ(2.1 % C) + Fe3C (6.67% C).
The eutectic mixture of austenite (γ) and cementite (Fe3C) is called Ledeburite.

5. The eutectoid mixture of ferrite (α) and cementite (Fe3C) is called __________
a) Ledeburite
b) Pearlite
c) Hyper and hypo eutectoid steel
d) Cast iron
Answer: b
Clarification: The pearlite is formed under equilibrium
Conditions which consists of alternate lamellas or layers of ferrite and Fe3C.

6. Compositions right and left of 0.8% C of Pearlite are called __________
a) Ledeburite
b) Ferrite
c) Hyper and Hypoeutectoid steel
d) Cast iron
Answer: c
Clarification: Hypoeutectoid steels – α+ p; hypereutectoid – Fe3C + p.

7.Compositions above 2.1% C is called as _______
a) Ledeburite
b) Ferrite
c) Hyper and Hypoeutectoid steel
d) Cast iron
Answer: d
Clarification: Compositions up to 2.1% of Carbon are considered steels and beyond this it is considered as cast iron.

8. From the following figure if Diffusion rates below Ms is so low that γ → M transformation is a diffusionless process then what is change in crystal structure
materials-science-questions-answers-online-quiz-q8
a) FCC → BCT
b) FCC → BCC
c) BCC → BCT
d) BCT → BCC
Answer: a
Clarification: Diffusion rates below Ms is so low that γ → M transformationis a diffusion less process (the C content remains same). However, the crystal structure changes from FCC (γ) to body centered tetragonal (BCT).

9.Finer size pearlite is called _______
a) Troostite
b) Ledeburite
c) Ferrite
d) Sorbite
Answer: d
Clarification: Finer size pearlite is called sorbite and very fine size pearlite is called troostite.

10. A eutectoid steel is slowly cooled from a temperature of 750°C to a temperature just below 727°C. Calculate the percentage of ferrite and cementite.
a) 88.3% and 11.7%
b) 70% and 30 %
c) 85.4% and 14.6%
d) 20% and 20%
Answer: a
Clarification: Eutectoid composition – 0.8% of Carbon,
Ferrite composition- 0.025% of Carbon and
cementite – 6.67% C.
Apply the lever rule to get the percentages as
% of Ferrite = 100(6.67 – 0.80)/(6.67 – 0.025)=88.3% ferrite
%of Cementite = 100(0.80 – 0.025)/(6.67 – 0.025) =11.7%.